Abstract
Failure behavior of polycarbonate(PC) under pure shear and simple tension was investigated in air at high temperature. Only shear flow with clear shear bands was observed under pure shear. Under simple tension, however, craze formation occurred at lower stress, and then shear flow was also observed at higher stress. The critical stresses for shear flow under both stress states were lower than those at room temperature. The shear flow was confirmed to obey the modified Tresca criterion. It was concluded that the craze formation does not occur when the shear flow precedes.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: The Proceedings of Conference of Hokuriku-Shinetsu Branch
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.