Abstract
In this research, the composites (100-x)LCP-xBNT (x = 0, 10, 20, 30, 40 vol.%) were fabricated with thermoplastic LCP(Liquid Crystal Polymer) and BNT(<TEX>$BaNd_2Ti_4O_{12}$</TEX>) which is a high frequency dielectric material. Their dielectric properties, mechanical strength and microstructure were investigated by Impedance analyser, Instron and SEM. In order to fabricate LCP-BNT composites, LCP resin was put into the twin screw type mixer(<TEX>$310^{\circ}C$</TEX>), melted by keeping for 10 min. After that, BNT filler was dispersed with melted LCP resin for 15 min. in the mixer. For measuring the dielectric properties and mechanical strength, Composite specimens were made by pressing composite granule (LCP-BNT) with 7 ton in the mold at <TEX>$310^{\circ}C$</TEX>. With increasing the BNT content (0~40 vol.%) of the composite, Its dielectric constant increased, dielectric loss and flexural strength decreased. The dielectric constant and flexural strength of composites with 20~30 vol.% of BNT filler are 4.1~6.0 and 35~55 MPa respectively. BNT/LCP composite is the potential substrate material for the high frequency application.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Korean Institute of Electrical and Electronic Material Engineers
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.