Abstract
인피섬유로 한지를 제조하고 남은 닥나무 목질부를 고부가가치화 하기 위하여 닥나무 목질부로 파티클 보드를 제조하고 페놀수지 함침율 변화에 따른 닥나무재료 우드세라믹을 제조하여 물성을 검토하였다. 밀도, 휨강도성능, Brinell 경도, 압축강도 등은 수지함침량이 증가할수록 증가하였으며 밀도와 휨강도성능, 경도, 압축강도간 및 휨탄성계수와 강도간에는 유의성이 인정되는 밀접한 상관관계를 나타내었다. This study was carried out to investigate the properties of woodceramics made from woody part of Broussonetia Kazinoki at different impregnation ratios of phenolic resin of 40, 50, 60, 70%. The physical and mechanical properties increased with increasing impregnation ratio. The highest mean values of density, bending strength, Brinell hardness and compressive strength were 0.66 g/<TEX>$cm^3$</TEX>, 53 kgf/<TEX>$cm^2$</TEX>, 187 kgf/<TEX>$cm^2$</TEX>, 126 kgf/<TEX>$cm^2$</TEX>, respectively. There were close correlations between density and bending strength, Brinell hardness and compressive strength, and between MOE and MOR.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.